Sintesis Komposit Nanopartikel Magnetit dan Karbon Aktif sebagai Absorber Gelombang Elektromagnetik

DSpace/Manakin Repository

Show simple item record

dc.contributor.author Suarni
dc.date.accessioned 2017-08-11T12:48:07Z
dc.date.available 2017-08-11T12:48:07Z
dc.date.issued 2017-08-11
dc.identifier.uri http://repository.unhas.ac.id/handle/123456789/25206
dc.description.abstract Sintesis nanokomposit magnetit dan karbon aktif dengan penambahan polyvinil alcohol (PVA) sebagai absorber gelombang elektromagnetik, telah berhasil dibuat dengan variasi ketebalan 4 mm, 6 mm, 8 mm, dan 10 mm. Karakterisasi XRD dilakukan untuk mengontrol terbentuknya magnetit (Fe3O4) serta menentukan ukuran kristal. Puncak difraksi untuk Fe3O4 adalah (331) pada sudut 35,81o dan (440) pada sudut 62,91o sesuai dengan JCPDS (joint commite on powder diffraction standars) no. Ukuran kristal magnetit (Fe3O4) adalah 0,11 nm. Karakterisasi XRF menunjukkan komposisi kimiawi absorber yang menunjukkan terbentuknya nanokomposit, spektrum FT-IR yang diperoleh menunjukkan adanya ikatan C=C alkena dan C-H alkana yang berasal dari karbon aktif, kertas honeycomb serta magnetit (Fe3O4) sehingga berkontribusi dalam pembentukan ikatan molekuler dari nanokomposit absorber. Karakterisasi Vector Network Analyzer (VNA) dengan frekuensi 2,5 GHz- 8 GHz diperoleh nilai reflectin loss yaitu 17,71 dB pada rentang frekuensi 5,5- 6 GHz dengan ketebalan 10 mm. Nanocomposite synthesis of magnetite and activated carbon with the addition of polyvinyl alcohol (PVA) as an absorber. Electromagnetic wave has been created with the thickness variation are 4 mm, 6 mm, 8 mm and 10 mm. XRD characterization is done to control the formation of magnetite (Fe3O4) and determine the size of the crystals. Diffraction peak of Fe3O4 is (331) at an angle of 35.81O and (440) at an angle of 62.91O in accordance with the JCPDS(Jointcommite on powder diffractionstandars) no. The size of the crystals of magnetite (Fe3O4) is 0.11 nm. XRF characterization show the formation of the nanocomposite of the chemical composition absorber, the FT-IR spectrum showed a C = C bonds of alkenes and alkane CH derived from activated carbon, paper honeycomb and magnetite (Fe3O4) that contribute to the formation of bonding molecular nanocomposite absorber. Vector Network Analyzer (VNA) characterization used a frequency of 2.5 GHz 8 GHz obtained the value reflectinloss is 17.71 dB in the frequency range 5.5 to 6 GHz with a thickness of 10 mm. en_US
dc.subject Gelombang Elektromagnetik, Magnetit (Fe3O4), Karbon Aktif, Absorber, Vector Network Analyzer dan Reflection Loss. en_US
dc.title Sintesis Komposit Nanopartikel Magnetit dan Karbon Aktif sebagai Absorber Gelombang Elektromagnetik en_US
dc.type Article en_US
dc.UNHAS.email suarnikhumaerah95@gmal.com en_US
dc.UNHAS.Fakultas MIPA en_US
dc.UNHAS.Prodi FISIKA en_US
dc.UNHAS.idno H21113007 en_US


Files in this item

This item appears in the following Collection(s)

Show simple item record

Search Repository


Browse

My Account